Anti-rust method and rust cause analysis of full complement bearing.com/cylindrical-roller-bearings.html' target='_blank'>cylindrical roller bearings: 1. Method of applying anti-rust oil The method of applying a layer of anti-rust grease. Oil film thickness can be achieved by controlling the temperature or viscosity of the anti-rust grease. b. The brushing method is used for outdoor construction equipment or special-shaped products that are not suitable for immersion or spraying. When brushing, attention should be paid not only to avoid accumulation, but also to prevent leakage. c. Spray method Some large anti-rust objects cannot be oiled by immersion method. Generally, the rotary table bearing is sprayed with filtered compressed air with a pressure of about 0.7Mpa in a clean air place. The spray method is suitable for solvent-diluted anti-rust oil or thin-layer anti-rust oil, but perfect fire protection and labor protection measures must be adopted. 2. The main factors of metal corrosion Metal corrosion is caused by various internal and external factors, which can be summarized as follows: a. The chemical composition and structure of the metal material itself; b. ); c. The composition and pH value of the solution in contact with the metal surface of the thrust cylindrical roller bearing; d. Ambient temperature and humidity; e. Various environmental media in contact with the metal surface. 3. Analysis of the reasons for the corrosion of steel: 1. Chemical corrosion of the steel Certain components in stainless steel parts react chemically, resulting in chemical corrosion and rust. (2) Surface scratches The damage to the passivation film by various scratches reduces the protection ability of stainless steel. What precautions should be taken in the installation and use of self-priming pumps? It is easy to react with chemical media, resulting in chemical corrosion and rust. (3) Cleaning After pickling and passivation, the cleaning is not clean, resulting in residual liquid remaining, which directly corrodes stainless steel parts (chemical corrosion). 2. Electrochemical corrosion of stainless steel 1) Carbon steel pollution The scratches caused by contact with carbon steel parts and the corrosive medium form galvanic cells and cause electrochemical corrosion. (2) Cutting female The adhesion of rust-prone substances such as cutting slag and cross roller bearing splash and corrosive medium form a primary battery and cause electrochemical corrosion. (3) Baking school The composition and metallographic structure of the flame heating area change unevenly, and form a galvanic cell with the corrosive medium to produce electrochemical corrosion. (4) Physical defects (undercut, pores, cracks, lack of fusion, lack of penetration, etc.) and chemical defects (coarse grains, poor chromium at grain boundaries, segregation, etc.) in the welding area and corrosive media form galvanic cells to generate electricity. Chemical corrosion Hpsdw5. (5) Material Chemical defects (uneven composition, S, P impurities, etc.) and surface physical defects (porosity, blisters, cracks, etc.) of stainless steel are conducive to the formation of galvanic cells with corrosive media to produce electrochemical corrosion. (6) Passivation The poor passivation effect of pickling will cause the passive film on the stainless steel surface to be uneven or thin, and it is easy to form electrochemical corrosion. (7) Cleaning The remaining pickling passivation residue and the products of chemical corrosion of stainless steel form electrochemical corrosion with stainless steel parts. 3. Stress concentration is easy to cause stress corrosion. In short, car rental and carpooling should be properly guided. Due to its special metallographic structure and surface passivation film, stainless steel is generally difficult to chemically react with the medium and be corroded. It cannot be corroded under any conditions. In the presence of corrosive media and incentives (such as scratches, splashes, slag cutting, etc.), stainless steel can also be corroded by slow chemical and electrochemical reactions with corrosive media, and the corrosion rate is quite fast under certain conditions. Corrosion phenomenon, what are the precautions for the installation and use of the self-priming pump? Especially pitting and crevice corrosion. The corrosion mechanism of stainless steel parts is mainly electrochemical corrosion. Therefore, all effective measures should be taken during the processing of stainless steel products to avoid corrosion conditions and incentives as much as possible. In fact, many rust conditions and inducements (such as scratches, splashes, cutting slag, etc.) also have a significant adverse effect on the appearance quality of the product, and should and must be overcome.
Over the years, has become very popular as more and more people are trying it out.
HangZhou Jnsn Bearing Imp& Exp Co., Ltd is committed to attracting, developing, and keeping a diverse work force that reflects the nature of our global business.
Rewards and discount programs give customers more reason to come back for CONTACT US again, especially in the competitive retail and services markets.
There have been conclusive evidence on 's role in Bearing Suppliers and Hrb Bearing China.
The stability of the system, controllability of the Bearing Suppliers process, and mobility of the machines provide with a flexible and reliable CONTACT US system.